Influence of the anion nature on the properties of Sr-containing formamidinium tin halide perovskites

摘要

Formamidinium-tin-strontium halides (CH(NH2)(2)Sn1-ySryX3 (FASnX(3)), X = I, Br and 0.0 = y = 0.1) were investigated. X-ray diffraction analysis revealed orthorhombic FASnI(3) (space group Amm2) and SnI2 for X = I as well as cubic FASnBr(3) (space group Pm3m) and SnBr2 for X = Br, respectively. For X = I, the optical spectra displayed a decrease of the absorption edges with increasing Sr content (1055 nm, y = 0.0; 950-960 nm, y 0.0) and a direct semiconducting behavior with narrow band energy gaps (1.31-1.34 eV). For X = Br, on increasing the absorption edges (492 nm, y = 0.0; 975 nm, y = 0.075), a direct semiconducting behavior with band energy gaps between 2.65 eV (y = 0.0) and 1.38 eV (y = 0.075) were observed and the emission photoluminescence (PL) spectra (excitation wavelength lambda(exc) = 380 nm) showed an increase of the luminescence response after the thermal treatment.