The grain size effect on the magnetic properties in NiZn ferrite and the quality factor of the inductor

摘要

Polycrystalline ferrite materials with the chemical composition of Ni_(0.49)Zn_(0.49)Co_(0.02)Fe_(1.90)O_x have been fabricated using the conventional ceramic sintering method. Grain sizes have been adjusted from ～2.2 to ～13.5 μm with changing sintering conditions. From the measurements of the complex permeability, it is suggested that the permeability is dominated only by the spin rotation at mono-domain state and both domain wall and spin rotation contribute at multi-domain state. At mono-domain state, the core loss has been drastically decreased similar to the other work. The measurement result for the loss angle indicates that the low loss state can be maintained up to the higher magnetic field with smaller grain size in spite of the mono-domain state. The simplified wire-wounded type inductors have been also fabricated and characterized. The results have shown that the inductor fabricated with the smaller grain size has a better performance in the quality value under relatively higher current.