Fatigue Life Prediction of Thick-Section S2-Glass/Vinyl- Ester Composites Under Flexural Loading

摘要

Fatigue life prediction of S2-Glass/Vinyl-ester composites has been studied analytically using the fatigue modulus concept. Traditionally it is assumed that the fatigue modulus degradation is a function of loading cycle only. In our present investigation, it is found that the fatigue modulus is not only a function of loading cycle but also a function of applied stress level and thickness of the specimen. Using this concept, a practical and applicable method for predicting fatigue life is established. The method requires two distinct parameters that arise from the mathematical formulation.