Thermal Management and Interfacial Properties in High-Power GaN-Based Light-Emitting Diodes Employing Diamond-Added Sn-3 wt.%Ag-0.5 wt.%Cu Solder as a Die-Attach Material

摘要

The thermal management of high-power GaN-based light-emitting diodes (LEDs) soldered with Sn-3 wt.%Ag-0.5 wt.%Cu (SAC305) solder and diamond-added SAC305 solder was evaluated. Diamond addition was found to significantly reduce the surface temperature and total thermal resistance of the LEDs, revealing that diamond-added SAC305 solder is a promising die-attach material for high-power LED packaging. Interfacial reactions in the LED solder joints were also investigated. The thin Au wetting layer in the chip’s backside metallization was rapidly consumed in the initial stage of reflow, forming an AuSn₄ phase at the interface. Subsequently, the AuSn₄ phase detached from the interface, leading to dewetting of the SAC305 solder from the LED chip. To avoid dewetting, a new backside metallization of LED chips should be developed for SAC305 solder.