Influence of Crosslink Density, Glass Transition Temperature and Addition of Pigment and Wax on the Scratch Resistance of an Epoxy Coating

摘要

The scratch resistance of a series of cationically cured epoxy coatings with varying crosslink densities has been investigated using five different scratch tests. The tests simulate a variety of scratch modes, ranging from single scratches to repeated surface wear. The relative influences of crosslink density and glass transition temperature on scratch resistance, as well as the effects of adding pigment and wax to the coatings, were examined. The results show the scratch resistance to increase both with increasing crosslink density and increasing glass transition temperature in all tests. It is also shown that adding pigment or wax either increased or decreased the scratch resistance of the coating, depending on which type of scratching was performed.%La resistencia al rayado de una serie de recubrimientos, epóxicos curados canónicamente con variación en la densidad del reticulado han sido investigados usando cinco diferentes pruebas de rayado. Estas pruebas simulan una variedad de formas de rayado, que varían desde el rayado sencillo hasta el rayado repetido de una superficie desgastada. Fueron estudiadas la influencia relativa de la densidad de reticulación y de la temperatura de transición vitrea sobre la resistencia al rayado, as! como también el efecto de la adición de pigmentos y ceras en el recubrimiento. Los resultados mostraron que la resistencia al rayado se incrementa cuando se incrementa la densidad de reticulación y la temperatura de transición vitrea al mismo tiempo en todas la pruebas. También se demostró que la adición de pigmentos y ceras cualquiera de los dos, aumenta o disminuye la resistencia al rayado del recubrimiento dependiendo de cual tipo de rayado se va a mejorar.