プレス成形時の部品重量変動を低減する偏析防止処理鉄粉「JIP~®クリーンミックス~®ZERO」の開発

摘要

The segregation-free iron powder JIP~® Cleanmix ZERO reducing variation in weight of green parts in powder metallurgy mass productive pressing line has been developed. It can improve the yield in the manufacturing process of the sintering part. When compaction pressing of continuous operation is restarted after the stop due to the unexpected reasons or break, Cleanmix ZERO can lower the difference between weight of parts before and after the stop. In addition, it contributes to superior filling ability to a die cavity and uniform filling in a cylinder cavity in simulated die for bush shape products. It results in the reduction of failures due to deviation from specification for part weight and dimensions at the time of the molding. These characteristics could be realized by reducing the adhesion between the particle. It was confirmed that cohesion of Cleanmix ZERO was less than half of usual Cleanmix powder in the powders layer shear examination.%焼結部品の製造プロセスにおける歩留まり向上を目的とし，成形時の部品重量変動の小さい偏析防止処理粉JIP~®クリーンミックス ZEROを開発した。クリーンミックスZEROは，連続成形中の不意な停止や休憩時の停止の後，成形を再開するときに，停止前の重量と再開直後の重量差を小さくできる。また，金型キヤビティーへの充填性にも優れ，ブッシュ状製品用の金型を横した円筒キャビティーに均一に充填することができる。これらにより，成形時の部品重量や寸法の規格はずれによる不良を低減することができる。これらの特長は，粒子間の付着力を低減することで実現でき，粉体層せん断試験では，クリーンミックスZEROのせん断付着力は，従来材の半分以下になっていることが確認された。