引張強さ1300MPa級および1500MPa級の焼結材料を製造可能なNiフリー合金鋼粉

摘要

JFE Steel has developed new grades of Ni-free alloyed steel powders, "JIP~® FM1300" and "JIP~® FM1500", with tensile strengths of 1300 MPa and 1500 MPa, respectively, after sintering and heat-treatment. "FM1300" is a Mo-prealloyed steel powder with diffusion bonded Mo fine particles on the steel particle surfaces for acceleration of inter-particle atomic diffusion during sintering and improvement of mechanical strength of sintered products. "FM1500" includes Cr and Mn as well as Mo for further improvement of the hardenability effect. The newly developed powders show almost homogeneous microstructures after sintering at high temperatures (≥1200℃), and give the tensile ： strengths mentioned above after appropriate heat-treatments. In conjunction with the products developed previously, JFE Steel has lined up Ni-free alloyed steel powders suitable for a wide range of applications requiring tensile strength from 600 MPa to 1500 MPa.%JFEスチールではNiフリー高強度合金鋼粉の新グレードとして,焼結・熱処理後の引張強さが1300MPa級の「JIP~®FM1300」，および1500MPa級の「JIP~®FM1500」を開発した。「FM1300」では，合金成分であるMoの一部を粒子表面に拡散付着させ，焼結を促進させることにより強度向上を図った。また，「FM1500」では，合金元素としてMoとともにCrおよびMnを添加することで，それらの相乗効果によって焼入れ性を高めた。両者のいずれについても，高温焼結を施すことによってほぼ均一な組織ビなり，適切な条件で熱処理することでそれぞれの目標の引張強さが得られる。既開発鋼粉ビ併せて600～1500MPa級の広い強度範囲の用途に対応した，Niフリー合金鋼粉がラインアップ化された。