Reaction mechanism between solid CaO and FeO_x-CaO-SiO_2-P_2O_5 slag at 1573 K

摘要

Solid CaO and FeO_x-CaO-SiO_2-P_2O_5 slag were reacted for 2 to 2 400 s at 1 573 K. The interface of CaO and slag were observed and analyzed by SEM/EDS. The CaO-FeO layer was formed beside solid CaO. The thickness of the CaO-FeO layer increased with time. Next to the CaO-FeO layer, 2CaO-SiO_2 phase was formed in the melt and high content of FeO was included in the liquid. The activities of FeO and CaO for each phase were evaluated and reaction mechanism between solid CaO and FeO_x-CaO-SiO_2-P_2O_5 slag was discussed. The activity of FeO for 2CaO-SiO_2 saturated melt is larger than that for the CaO-FeO layer, therefore, Fe~(2+) diffuses from slag phase to solid CaO. Then the CaO-FeO layer is formed beside solid CaO. The pass of the slag composition change accompanied by CaO dissolution are represented in the phase diagram for the FeO_x-CaO-(SiO_2+P_2O_5) pseudo ternary system.