Mechanically activated Pt-Ni and Pt-Co alloys as electrocatalysts in the oxygen reduction reaction

摘要

Mixtures of powders of platinum with nickel or cobalt to obtain Ni_(0.75)Pt_(0.25) or Co_(0.75)Pt_(0.25) were mechanical alloyed by high energy ball milling. The results of crystal structure, morphology and electrocatalytic performance are presented for mechanically activated powders after 3 and 9 h of ball milling. Total solid solutions of Ni and Co with platinum were analyzed by X-ray diffraction after 3 h of ball milling. After 9 h of ball milling, in both cases, the total solid solution was accompanied by the appearance of NiO or CoO and ZrO associated with a redox reaction with the milling media. The presence of zirconium monoxide was confirmed by energy dispersive spectroscopy analysis. In both cases, an amorphization was detected. X ray absorption spectroscopy measurements showed changes in atomic and electronic environment of platinum, a reduction of the distance to the first coordination sphere and increased d-band vacancy vs pure Pt and Pt nanoparticles were observed for both studied systems. The electrocatalytic activity was determined using cyclic and linear voltammetry. The Co_(0.75)Pt_(0.25) alloy milled for 9 h showed a higher electrochemical activity for the oxygen reduction reaction (ORR) compared with the other samples, including Pt-Etek. The degree of the ORR electrochemical activity was correlated with the presence of ZrO, which could affect the oxygen adsorption and improve the catalytic activity for the oxygen reduction reaction.