Abnormal effect of nitrogen on hydrogen gas embrittlement of austenitic stainless steels at low temperatures

摘要

Hydrogen gas embrittlement (HGE) of nitrogen alloyed 316 series austenitic stainless steels was investigated in the temperature range from 80 K to 300 K. Nitrogen and nickel have the same stabilizing ability for austenite, while they show different effect on HGE. Above 200 K, both nitrogen and nickel weaken HGE with decreasing strain induced alpha' martensite, but HGE of nitrogen alloyed steels is severer than that of nickel alloyed steels in the case of the same a' martensite content. At 150 K, almost no HGE is found in nickel alloyed 316 steels, while nitrogen causes an abnormal increase of HGE at 150 K. There are two factors influencing HGE in nitrogen alloyed 316 steels at low temperatures: one is planar slip caused by nitrogen; the other is hydrogen transport by dislocations in the localized shear slip band. It is evident that nitrogen-induced planar slip plays an important role in HGE of nitrogen alloyed 316 steels at low temperatures. (C) 2016 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.