机译:残余应力再分布和焊接焊接几何对抗杆焊接接头疲劳裂纹生长的影响
Faculty of Mechanical Engineering Department of Applied Mechanics K.N. Toosi University of Technology P.O. Box 19395-1999 Tehran Iran;
Fracture Mechanics Research Laboratory Department of Applied Mechanics K.N. Toosi University of Technology Tehran Iran;
Faculty of Aerospace Engineering Delft University of Technology Kluyverweg 1 2629 HS Delft the Netherlands;
Residual stress redistribution; Weld reinforcement geometry; Fatigue crack growth; Stress intensity factor; Welded joint;
机译:十字形焊接接头的疲劳裂纹扩展:残余应力和焊趾几何形状的影响
机译:考虑焊接引起的残余应力和初始损伤,残余应力的松弛以及弹塑性疲劳损伤的对焊接头疲劳寿命预测
机译:考虑焊接诱导的残余应力和初始损伤,放松残余应力,疲劳寿命预测对接焊接接头的疲劳寿命预测,以及剩余应力的放松,以及弹塑性疲劳损伤
机译:焊接残余应力对低合金对接焊接蠕变裂纹增长的影响
机译:几何形状和残余应力对焊接接头疲劳度的影响
机译:循环拉伸载荷下焊缝加固和焊接后冷却循环对对接焊缝疲劳强度的影响
机译:预测焊接对接接头的疲劳裂纹增长率:考虑残余应力效应的有效R比