As_2Se_3 カルコゲナイドガラスの非線形光学特性のパルス幅依存性とその発現機構

摘要

We investigate the pulse-width dependence of optical nonlinearities in As_2Se_3 glass by the Z-scan method. Two kinds of optical pulses were utilized for the Z-scan experiment; nanosecond optical pulses with a 1.064 μm wavelength whose duration was changed from 11.5 ns to 1.6 ns by the pulse compression using stimulated Brillouin scattering in a liquid and picosecond optical pulses with a wavelength of 1.053 μm. The experimental results show that both the nonlinear refractive index and the nonlinear absorption coefficient increase linearly with pulse width. The origin of such pulse-width dependence is presumably attributed to photostructural changes inherent in chalcogenide glasses by linear absorption in the weak-absorption region.%Z-スキャン法の光源のパルス幅を変化させることにより，As_2Se_3 ガラスの非線形光学特性のパルス幅依存性の測定を行った．SBS パルス圧縮技術を用いてパルス幅を11.5ns から1.6ns まで変化させたNd:YAG レーザ光（波長：1.064pm）とパルス幅60ps のYLFレーザ光（波長：1.053μm）を用いて測定した結果，非線形屈折率および非線形吸収係数の符号は共に正で，その大きさはパルス幅に対して直線的に増加した．このパルス幅に依存した非線形性は，熱効果やキャリア効果ではなく，線形吸収によって引き起こされた光構造変化によるものであると思われる．