Influence of surface roughness on magnetic properties of Fe-Si-B amorphous alloys

摘要

Influence of surface roughness on magnetic properties of Fe/sub 78/Si/sub 9/B/sub 13/ and Fe/sub 78/Si/sub 14/B/sub 8/ amorphous alloy ribbons was investigated. Magnetic induction in an external field of 800 A/m, B/sub 8/ of Fe/sub 78/Si/sub 9/B/sub 13/ ribbon increased slightly with decreasing surface roughness, while iron loss W/sub 13/50/, at 1.3 T 50 Hz excitation, remained almost at the same level. In Fe/sub 78/Si/sub 14/B/sub 8/ amorphous alloy, however, quite different behaviors were observed. Both B/sub 8/ and W/sub 13/50/ were improved remarkably with decreasing surface roughness of the ribbon. Fe/sub 78/Si/sub 14/B/sub 8/ amorphous ribbon showed as good a magnetic performance as Fe/sub 78/Si/sub 9/B/sub 13/ only if it had a smooth surface. The drastic improvement of iron loss with decreasing surface roughness was mainly due to the decrease in hysteresis loss. According to the analysis of the iron loss and surface roughness of the ribbons, it was considered that gentle and large undulations of the ribbon surface did not prevent the domain wall from moving, but steep and small irregularities such as air pockets pinned the domain wall. This behavior seems to be caused by the different mechanism of domain wall pinning in these two amorphous alloys.