Elektrochemische und mechanische Eigenschaften von Bleilegierungsanoden

摘要

The mechanical, electrochemical and corrosion behaviour of alloys of the systems Pb-Ag, Pb-Ag-Ca, Pb-Sn-Ca and Pb-Sb is investigated in several synthetic sulphuric acid solutions and in technical zinc electrolyte. The aim was a comprehensive evaluation of the lead based alloy anodes referring to their use in technical metal winning electrolysis. Analyzing the results, a rolled PbSn1,4Ca0,12-alloy (Prengaman-anode) shows excellent mechanical features and the lowest corrosion rate in the test, but the anode potential reaches the range of pure lead anodes. For a zinc winning electrolysis, a PbAg0,5 alloy is the best compromise. An addition of Mn~(2+) ions corresponds to a decrease of the oxygen overpotential of nearly 70 mV.%An Legierungen der Systeme Pb-Ag, Pb-Ag-Ca, Pb-Sn-Ca und Pb-Sb wurden Untersuchungen zum Kriechverhalten, zur Korrosionsrate und zu den elektrochemischen Eigenschaften in verschiedenen synthetischen schwefelsauren Lösungen sowie im technischen Zinkelektrolyt durchgeführt. Ziel der Untersuchungen war die umfassende Bewertung von Bleilegierungsanoden bezüglich ihres Einsatzes in der technischen Gewinnungselektrolyse. Die Ergebnisse verdeutlichen, daß die gewalzte PbSn1,4Ca0,12-Legierung (Prenga-man-Anode) hervorragende mechanische Eigenschaften bei der im Vergleich geringsten Korrosionsrate aufweist, wobei sich allerdings Anodenpotentiale im Bereich von reinem Blei einstellen. Für die Zinkgewinnungselektrolyse ist eine PbAg0,5-Legierung ein optimaler Kompromiß. Der Zusatz von Mn~(2+)-Ionen bewirkt bei allen Legierungen eine Depolarisation der Sauerstoff-abscheidung um ca. 70 mV.