Evaluation of electrochemical impedance and biocorrosion characteristics of as-cast and T4 heat treated AZ91 Mg-alloys in Ringer's solution

摘要

The present study aims at understanding the electrochemical impedance and biocorrosion characteristics of AZ91 Mg-alloy in Ringer's solution. As-cast AZ91 Mg-alloy was subjected to T4 heat treatment in a way to homogenize its microstructure by dissolving most of theβ-Mg17Al12phase at the vicinity of grain boundaries. The electrochemical impedance and biocorrosion performances of these two different microstructures (as-cast and T4 heat treated AZ91 Mg-alloys) in Ringer solution were evaluated by electrochemical impendence spectroscopy, potentiodynamic polarization and weight loss method. EIS spectra showed that both microstructures exhibit similar dynamic response as a function of the immersion time; however, the value of impedance and maximum phase angle are about 50% higher in as-cast AZ91 Mg-alloy as compared to that of homogenized AZ91 Mg-alloy. Weight loss measurement indicated that corrosion resistance of as-cast AZ91 was significantly better than that of homogenized AZ91. Microstructural and XRD analysis revealed that as-cast AZ91 contains a passive film of MgCO3and CaCO3precipitates with near spherical morphologies, whereas homogenized AZ91 comprised mainly unstable Mg(OH)2film featured by irregular plate-like morphologies.