Fracture toughness of seven resin composites evaluated by three methods of mode I fracture toughness (K_Ic)

摘要

This study compared the fracture toughness values of seven resin composites and analyzed the consistency of data values using three methods: compact tension, three point and four point bending for Mode I failure. Seven resin composites were selected: Estellite Sigma Quick, Esthet X HD, Filtek Supreme XTE, Heliomolar, Ice, Rok, and Vit-l-escence. For each material, 18 specimens (n =6 for each test) were prepared. Maximum load to failure was recorded using a universal testing machine and fracture toughness was calculated. There was a direct significant correlation among all tested methods. Rok showed the highest and Estelite the lowest K _(Ic) values. SEM of the fractured surface of compact tension method showed propagation of the cracks from stresses concentrating at the corner of the notch and the surface of the sample. Four-point test gave the largest range in K _(Ic) and was a simple method to discriminate between the resin composite values of K _(Ic).