Reversible Control of Primary and Secondary Self-Assembly of Poly(4-allyloxystyrene)-Block-Polystyrene

摘要

The reversible control of primary and secondary self-assemblies was attained using a poly(4-allyloxystyrene)-block-polystyrene diblock copolymer (PASt-b-PSt) through variations in temperature. The copolymer showed no self-assembly in cyclohexane over35∘Cand existed as a unimer with a 37.1 nm hydrodynamic diameter. When the temperature was lowered to30∘C, the copolymer formed micelles with 269.9 nm by the primary self-assembly. As the result of further lowering the temperature to20∘C, the secondary self-assembly of the micelles occurred to produce ca. 2975.9 nm aggregates. The aggregates were dissociated into unimers by increasing the temperature up to40∘C. The light scattering studies demonstrated that the thermoresponsivity of the copolymer showed good hysteresis throughout the variation in the temperature in the range between 20 and40∘C, based on the Marquadt analysis of the hydrodynamic diameter distribution. It was found that the primary and secondary self-assemblies of the copolymer were perfectly controlled by the temperature.