The use of Red Cabbage’s anthocyanine extract as a photosensitizer on a Dye-Sensitized Nanocrystalline TiO2 Solar Cell. A solid-state dye-sensitized nanocrystalline TiO2 solar cell utilizing anthocyanin extract form red cabbage as photosensitizer was fabricated. The solar cell was formed in sandwich structure, which two electrodes sandwiching polymer electrolyte containing a redox couple (I-/I3-). One of the electrodes, namely working electrode, TiO2 layer on TCO (transparent conducting oxide) coated glass substrate was sensitized with anthocyanin dye as electron donor in the system. Another electrode was a carbon sheet as a counter electrode. Gel electrolyte based on PEG (polyethylene glycol) containing a redox couple (I-/I3-) used instead of liquid electrolyte in this photoelectrochemical cell. Two fabricated cells have an active area of 1 cm2 were soaked with anthocyanine dye for 1 hr and 24 hrs, respectively. The cells were tested by irradiation with halogen lamp of 24 Watt with intensity 4 mW/cm2 at a distance 30 cm. The testing results of the cells show an ideal I-V characteristic with output parameters: open circuit voltage (VOC) of 500 mV, short circuit current (ISC) of 5,6 μA and 7,2 μA for each cells, fill factor (FF) of 48% for both cells, energy conversion (η) of 0.023% and 0,055% for the cells with 1 hr and 24 hrs dye soaked, respectively. Abstract in Bahasa Indonesia: Telah dipabrikasi sel surya TiO2 nanokristal padat tersensitisasi dye menggunakan ekstrak antosianin dari kol merah sebagai fotosensitizer. Sel surya dibentuk dengan struktur sandwich, dimana dua elektroda mengapit elektrolit polimer yang mengandung kopel redoks I-/I3-. Salah satu elektroda, yaitu elektroda kerja berupa lapisan TiO2 pada substrat kaca berlapis bahan TCO (transparent conducting oxide) disensitisasi dengan dye antosianin sebagai donor elektron dalam sistem sel surya ini. Elektroda lain berupa lempengan karbon sebagai elektroda lawan. Elektrolit gel berbasis PEG (polyethylene glycol) mengandung kopel redoks I-/I3- digunakan sebagai pengganti elektrolit cair pada sel fotoelektrokimia ini. Dua sel yang dipabrikasi memiliki luas 1 cm2 direndam dengan dye antosianin masing-masing selama 1 jam dan 24 jam. Sel-sel ini diuji dengan penyinaran menggunakan lampu halogen 24 Watt dengan intensitas 4 mW/cm2 pada jarak 30 cm. Hasil pengujian sel-sel ini memperlihatkan karakteristik I-V yang ideal dengan parameter keluaran: tegangan rangkaian buka (VOC) 500 mV, arus rangkaian pendek (ISC) 5,6 μA dan 7,2 μA untuk masingmasing sel, fill factor (ff) 48% untuk kedua sel, konversi energi (η) 0,023% dan 0,055% masing-masing untuk sel yang direndam dengan dye selama 1 jam dan 24 jam.
展开▼
机译：红甘蓝的花青素提取物在染料敏化的纳米TiO2太阳能电池上用作光敏剂。制备了利用红甘蓝中的花青素提取物作为光敏剂的固态染料敏化纳米晶TiO2太阳能电池。太阳能电池形成为三明治结构，其中两个电极将包含氧化还原对（I- / I3-）的聚合物电解质夹在中间。电极之一，即工作电极，TCO（透明导电氧化物）涂层玻璃基板上的TiO2层被花青素染料作为系统中的电子供体敏化。另一个电极是作为反电极的碳片。在该光电化学电池中，使用基于氧化还原对（I / I3-）的基于PEG（聚乙二醇）的凝胶电解质代替液体电解质。将两个制造的活性面积为1 cm2的电池分别用花青素染料浸泡1小时和24小时。通过用24瓦的卤素灯在距离30cm处以4mW / cm 2的强度照射来测试电池。电池的测试结果显示了理想的IV特性，具有以下输出参数：每个电池的开路电压（VOC）为500 mV，每个电池的短路电流（ISC）为5.6μA和7.2μA，填充系数（FF）对于两个电池，其能量转化率（η）分别为48％，对于浸有1小时和24小时染料的细胞，能量转化率（η）分别为0.023％和0.055％。印度尼西亚语中的摘要：Telah dipabrikasi sel surya TiO2纳米kristal padat致敏染料menggunakan ekstrak antosianin dari kol merah sebagai感光剂。 Sel surya dibentuk dengan struktur三明治，dimana dua elektroda mengapit elektrolit polimer yang mengandung kopel redoks I- / I3-。 Salah satu elektroda，yaitu elektroda，TiO2 pada substrat kaca berlapis bahan TCO（透明导电氧化物）二敏性丹参染料antosianin sebagai供体elektron dalam sistem sel surya ini。 Elektroda lain berupa lempengan karbon sebagai elektroda lawan。 Elektrolit凝胶berbasis PEG（聚乙二醇）mengandung kopel redoks I- / I3- digunakan sebagai pengganti elektrolit cair pada sel fotoelektrokimini。 Dua sel yang dipabrikasi memiliki luas 1 cm2 direndam dengan染料antosianin masing-masing selama 1 jam dan 24 jam。 Sel-sel ini diuji dengan penyinaran menggunakan lampu卤素24瓦Dengan强度4 mW / cm2 pada jarak 30厘米。 Hasil pengujian sel-sel ini memperlihatkan karakteristik IV杨理想dengan参数keluaran：tegangan rangkaian buka（VOC）500 mV，arus rangkaian pendek（ISC）5,6μAdan 7,2μAuntuk masingmasing sel，填充系数（ff）48％ untuk kedua sel，konversi能量（η）0,023％丹0,055％masing-masing untuk sel yang direndam dengan染料selama 1果酱dan 24 jam。
展开▼