机译:X70管线钢在高pH碳酸盐溶液中应力腐蚀开裂的电化学阻抗谱分析。
Tarbiat Modares University, Faculty of Engineering, Department of Material Science and Engineering, Jalal Ave., P.O. Box 14115-143, Tehran, Iran;
Tarbiat Modares University, Faculty of Engineering, Department of Material Science and Engineering, Jalal Ave., P.O. Box 14115-143, Tehran, Iran;
Tarbiat Modares University, Faculty of Engineering, Department of Material Science and Engineering, Jalal Ave., P.O. Box 14115-143, Tehran, Iran;
Tarbiat Modares University, Faculty of Engineering, Department of Material Science and Engineering, Jalal Ave., P.O. Box 14115-143, Tehran, Iran;
A.steel; B.EIS; C.stress corrosion;
机译:pH值对X70管线钢在稀碳酸氢盐溶液中的电化学和应力腐蚀开裂行为的影响
机译:X70管线钢在碳酸盐溶液中应力腐蚀开裂的EIS研究。
机译:X70管线钢在碳酸盐/碳酸氢盐溶液中的腐蚀的微电化学表征和Mott-Schottky分析
机译:X70管线钢在近中性pH溶液中应力腐蚀破裂的研究
机译:研究高强度管线钢在碳酸盐-碳酸氢盐溶液中的腐蚀和应力腐蚀开裂行为。
机译:交流干扰和阴极保护对X70管线钢在近中性pH环境下点蚀和应力腐蚀开裂行为的综合影响
机译:交流干扰和阴极保护对近中性pH环境中X70管道钢蚀腐蚀和应力腐蚀开裂行为的综合作用