Fatigue life prediction in a unidirectional glass-epoxy composite material subjected to off-axis cyclic loads

摘要

Most of today s fatigue analysis and design methods for composite laminates were developed primarily on the basis of experience with homogeneous metals. Such methods are subject to serious drawbacks, however, because the failure modes typical of the heterogeneity and directional microstructure of composite laminates differ substantially from the modes of failure observed in metals. A theoretical model for predicting the fatigue life of continuous glass-flbre/epoxy composite materials under general loading conditions has been developed on the basis of fundamental fatigue failure modes and local failure criteria.%La mayoría de los actuales métodos de cálculo y diseño a fatiga de estructuras de materiales compuestos se han desarrollado principalmente a partir de la experiencia previa en materiales metálicos homogéneos. Sin embargo, estos métodos presentan serios inconvenientes debido a que la heterogeneidad y micro estructura orientada características de los materiales compuestos laminados provocan modos de fallo diferentes a los de los metales. Basándose en los modos fundamentales de rotura por fatiga y en criterios de rotura local, se desarrolla un modelo teórico de vida a fatiga para materiales compuestos de matriz epoxi reforzados con fibra de vidrio bajo condiciones generales de carga.