Study on friction and wear behavior of polyphenylene sulfide composites reinforced by short carbon fibers and sub-micro TiO_2 particles

摘要

Polyphenylene sulfide (PPS) composites filled with short carbon fibers (SCFs) (up to 15 vol.%) and sub-micro-scale TiO_2 particles (up to 7 vol.%) were prepared by extrusion and subsequently injection-molding. Based on the results of sliding wear tests, the tribological behavior of these materials was investigated using an artificial neural network (ANN) approach. A synergistic effect of the incorporated short carbon fibers and sub-micro TiO_2 particles is reported. The lowest specific wear rate was obtained for the composition of PPS with 15 vol.% SCF and 5 vol.% TiO_2. A more optimal composition of PPS with 15 vol.% SCF and 6 vol.% TiO_2 was estimated according to ANN prediction. The scanning electron microscopy (SEM) observation revealed that this hybrid reinforcement could be interpreted in terms of a positive rolling effect of the particles between the two sliding surfaces, which protected the short carbon fibers from being pulled-out of the PPS matrix.