Effetto dello spinello MgAl_2O_4 sull'evoluzione delle proprietà meccanicochimiche e microstrutturali di una matrice refrattaria sinterizzata di MgO-CaZrO_3

摘要

The mechano-chemical and microstructural evolution using magnesium-aluminium spinel in a MgO-CaZrO_3 sintered refractory matrix acting as ceramic bonding was investigated. The microstructural study reveals MgAI_2O_4 spinel phase at contact points between MgO and CaZrO_3 particles. In addition, the cold crushing strength of the MgO-CaZrO_3 matrix increases with the addition of 2.5-3.5 wt% MgAI_2O_4 spinel, this being attributed to the strong bond formed between MgO and CaZrO_3 due to the MgAI_2O_4 spinel phase aid. Finally, this refractory matrix exhibits a good thermal stability and excellent chemical resistance against cement raw meal.%Èstata analizzata l'evoluzione meccanico-chimica e microstrutturale di una matrice refrattaria sinterizzata a base di MgO-CaZrO^_3 dopo inserimento di spinello magnesio-alluminio come legante ceramico, L'analisi microstrutturale rivela una fase spinello di MgAI_20_4neipunti di contatto fra le particelle di MgO e CaZrO_3. Si è inoltre osservato un aumento della resistenza a rottura a freddo della matrice MgO-CaZrO_3con aggiunta di 2,5-3,5% in peso di spinello MgAI_2O_4; tale fenomeno può essere attribuito al forte legame che sì forma fra MgO e CaZrO_3 grazie all'ausilio della fase spinello di MgAl_2O_4. Infine, tale matrice refrattaria è caratterizzata da buona stabilità termica ed ottima resistenza chimica rispetto ai materiali di carica per cemento.