CRYSTALLIZATION MECHANISM AND BIOACTIVITY OF LITHIUM DISILICATE GLASSES IN RELATION TO CaO, P_2O_5, CaF_2 ADDITION

摘要

The present investigation reports the results of P_2O_5, CaO and CaF_2 (in stechiometric ratio corresponding to fluoroapatite) effect upon the controlled crystallization of grain-sized particles of lithium disilicate (LS_2) glass and upon the bioactivity of given glasses, that have been investigated by means of DTA and by in vitro testing after 4 weeks, respectively. The crystallization of pure lithium disilicate glass as well as that of glass containing the above components proceeds by surface and internal mechanism as function of particle size. The onset of internal crystallization, which substitutes the surface one is found at about 0.3 mm for pure lithium disilicate glass, while this change occurred at size of 0.9 mm approximately in glass containing CaO, P_2O_5 and CaF_2. The addition of different amount of "apparent fluoroapatite" enhances the bioactivity of bio-glasses as confirmed by SEM and EPMA.%Prezentovaný výskurn referuje o vplyve P_2O_5, CaO a CaF_2 (v stechiometrickom pomere zodpovedajúcom zloženiu fluóra-patitu) na kontrolovánu kryštalizáciu róznych frakcií lítium dis-ilikátového skla, študovánú pomocou DTA, a na bioaktivitu příslušných skiel, ktorá bola študovaná prostredníctvom in vitro testovania. Kryštalizácia čistého lítium disilikátového skla rovnako ako skla obsahujúceho vyššie zmienené zložky pre-bieha v závislosti od vel''kosti častíc mechanizmom povrchovej alebo objemovej kryštalizácie. V prípade čistého lítium disilikátového skla sa objemová kryštalizácia, ktorá nahrádza povr-chovú kryštalizáciu, prejavila u častíc s vel''kosťou okolo 0.305 mm, zatial'' čo u skla obsahujúceho P_2O_5, CaO a CaF_2 bola zmena mechanizmu kryštalizácie detekovaná u častíc s vel''-kosťou okolo 0.90 mm. Prídavok róznych množstiev "fluóra-patitu" zlepšuje bioaktivitu týchto bioskiel, čo bolo potvrdené REM i EPMA.