Preparation, Characterization of Sulfur-Doped Nanosized TiO₂ and Photocatalytic Degradation of Methylene Blue Under Visible Light

摘要

Sulfur-doped TiO₂ catalysts were prepared by a mechanochemical method. The prepared catalysts exhibited photocatalytic activity in methylene blue degradation under visible light. The catalyst structure has been characterized using UV–visible spectroscopy, X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), transmission electron microscopy (TEM), thermogravimetry analysis (TGA) as well as Fourier transform infrared spectroscopy (FT-IR). UV–visible spectroscopy revealed that the absorption edge of the doped TiO₂ was red-shifted compared with bare TiO₂. XRD patterns suggested that the brookite phase became more prevalent with increasing ball milling duration. In addition, surface sulfate species were detected by FT-IR, XPS and TGA. We deduce the rise of catalytic activity is due to the synergetic effect between the brookite phase and the anatase phase that would probably retard the electron–hole recombination. On the other hand, methylene blue was found to be N-demethylated during the irradiation thus giving rise to blue-shifting of peak at 664 nm in UV–visible spectroscopy.