Cost-effective electrostatic-sprayed SrAl₂O₄:Eu2 + phosphor coatings by using salted sol–gel derived solution

摘要

3 Mol% of europium doped strontium aluminate (SrAl₂O₄:Eu2 + ) coatings on silicon substrates were prepared by electrostatic spray deposition method using a salted sol–gel derived solution as a starting material. As-deposited films at 100°C for 5 h were heated at 1100°C for 2 h under a reducing ambient atmosphere of 95%N₂ + 5%H₂. Nanocrystalline SrAl₂O₄ film was confirmed by surface morphological and crystallographic analyses. Monitored at 520 nm, the excitation spectrum showed a broad band from 300 ~ 500 nm and the emission intensity showed a maximum yellow peak intensity at 512 nm with a broad band from 460 ~ 610 nm.