Surface properties of nitrided layer on AISI 316L austenitic stainless steel produced by high temperature plasma nitriding in short time

摘要

It has generally been believed that the formation of the S phase or expanded austenite γ_n with enough thickness depends on the temperature (lower than 480 ℃) and duration of the process. In this work, we attempt to produce nitrogen expanded austenite layer at high temperature in short time. Nitriding of AISI 316L austenitic stainless steel was carried out at high temperatures (＞520 ℃) for times ranging from 5 to 120 min. The microstructures, chemical composition, the thickness and the morphology of the nitrided layer, as well as its surface hardness, were investigated using X-ray diffraction, X-ray photoelectron spectroscopy, optical microscopy, scanning electron microscopy, and microhardness tester. The corrosion properties of the untreated and nitrided samples were evaluated using anodic polarization tests in 3.5% NaCl solution. The results confirmed that nitrided layer was shown to consist of γ_n and a small amount of free-CrN and iron nitrides. High temperature plasma nitriding not only increased the surface hardness but also improved the corrosion resistance of the austenitic stainless steel, and it can critically reduce processing time compared with low temperature nitriding.