Direct evaluation of ballistic phonon transport in a multi-walled carbon nanotube

摘要

Phonon confinement and in situ thermal conductance measurements in an individual multi-walled carbon nanotube (MWNT) are reported. Focused ion beam (FIB) irradiation was used to successively shorten a 4.8 μm long MWNT, eventually yielding a 0.3 μm long MWNT. After the first FIB irradiation, a 41% reduction in conductance was achieved, compared with that of the pristine MWNT. This was because the contributions from phonons with long free paths were excluded by scattering at FIB-induced defects. Phonon transport in linked multiple-length nanotubes was also investigated.