Determination of the critical crack length for steam generator tubing based on fracture-mechanics-based method

摘要

The steam generator (SG) tubing, as a key ingredient in the primary coolant circuit, is the weakest link that affects the availability and safety of a nuclear power plant. For safety reasons, it is very important to predict the life span of SG tubing. The critical crack lengths at different stages should be determined when the life span can be predicted. In this article, the critical crack lengths at different stages are determined in the form of graphs based on fracture-mechanics approach. From these graphs, it is concluded that the critical crack lengths for fatigue, stress corrosion cracking (SCC), and rupture are 0.11 mm, 0.36 mm and 7.20 mm respectively under accident conditions, and 1 mm, 2 mm, 43 mm respectively under normal conditions. It can also be concluded that the crack propagation mechanism can be divided successively into three or four stages, namely the corrosion stage, the fatigue stage (if the load is turbulent), the SCC stage and the rupture stage. Finally, some advices for the accelerated life test are given.