Study on Precipitation and Growth of TiN in GCr15 Bearing Steel during Solidification

摘要

In this paper, the precipitation thermodynamics and growth kinetics of TiN inclusions in GCr15 bearing steel during solidification were calculated in more detail. A more reasonable formula for calculating the segregation of the solute elements was adopted and the stability diagram of TiN precipitation considering solidification segregation was given. By solving equations, the change of the solute element content before and after TiN inclusion precipitation was calculated, and the results were substituted into the kinetic formula of the inclusion growth, which made the kinetic calculation more accurate. Results showed that the most effective way to reduce the precipitation of TiN is to increase the cooling rate and decrease the contents of Ti and N in steel. The effect of Ti content on the size of TiN inclusions is greater than that of N content.