Lithium intercalation/de-intercalation behavior of a composite Sn/C thin film fabricated by magnetron sputtering

摘要

A tin film of 320 nm in thickness on Cu foil and its composite film with graphite of ～50 nm in thickness on it were fabricated by magnetron sputtering. The surface morphology, composition, surface distributions of alloy elements, and lithium intercalation/de-intercalation behaviors of the fabricated films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), electron probe microanalyzer (EPMA), X-ray photoelectron spectroscopy (XPS), inductively coupled plasma atomic emission spectrometry (ICP), cyclic voltammetry (CV), and galvanostatic charge/discharge (GC) measurements. It is found that the lithium intercalation/de-intercalation behavior of the Sn film can be significantly improved by its composite with graphite. With cycling, the discharge capacity of the Sn film without composite changes from 570 mAh/g of the 2nd cycle to 270 mAh/g of the 20th cycle, and its efficiency for the discharge and charge is between 90% and 95%. Nevertheless, the discharge capacity of the composite Sn/C film changes from 575 mAh/g of the 2nd cycle to 515 mAh/g of the 20th cycle, and its efficiency for the discharge and charge is between 95% and 100%. The performance improvement of tin by its composite with graphite is ascribed to the retardation of the bulk tin cracking from volume change during lithium intercalation and de-intercalation, which leads to the pulverization of tin.