Particular properties of Ti_2O and TiN_x nanoparticles prepared by thermal decomposition

摘要

Particular properties of Ti2O and TiNx prepared by thermal decomposition were introduced. A precursor prepared by titanium powder react- ing with oxalate acid was thermally decomposed in nitrogen atmosphere at 840°C for 15 min, and relatively pure Ti2O was then obtained. Conductive TiNx was also prepared after altering reaction conditions. Samples were characterized by resistivity, X-ray powder diffraction, transmission electron microscope, Ultraviolet-Visible diffuse reflection, and electromagnetic shielding efficiency. The results indicate that both Ti2O and TiNx have good conductivity. Moreover, Ti2O shows a better solar photocatalytic activity and TiNx does well in the electro- magnetic shield.