Morphological evolution of γ'precipitates in a nickel-based superalloy during various solution treatments

摘要

The morphological evolution of the γ' phase in nickel-based superalloy жc6y during various solution heat treatments was investigated. The significant changes of the γ' precipitates were observed in the solution-treated samples. The coarsening and dissolution of γ' phase simulta-neously occurred at intermediate temperatures. In some areas, the primary precipitates became blunt and the adjacent ones were intercon-nected with each other via a diffuse neck, indicating a coarsening process of the primary γ' population. The coarsening was dominated by the precipitate agglomeration mechanism (PAM) rather than by the well-known Ostwald ripening mechanism. In other areas, the partial dissolu-tion of the γ' precipitates began to occur, spreading gradually from dendrite cores to interdendritic regions. In addition, a flower-like γ' struc-ture was developed during the subsolvus solution treatments. The observable long filaments composed of erraticly shaped precipitates were caused by the heterogeneous nucleation of the cooling precipitates during water quenching.