Total conductivity,oxygen permeability and stability of perovskite-type oxide BaCo_(0.7)Fe_(0.2)Nb_(0.1)O_(3-δ)

摘要

The total conductivity,oxygen sorption property,oxygen permeability and stability of pure perovskite-type oxide BaCo0.7Fe0.2Nb0.1O3-δ (BCFNO) in real operating conditions were investigated. Its total conductivity was measured to be 3.6 S·cm-1 at 600°C. Though the total conductivity of the BCFNO membrane is much smaller than that of the Ba0.5Sr0.5Co0.8Fe0.2O3-δ (BSCFO) membrane,the oxygen permeability of the BCFNO membrane is similar to that of the BSCFO membrane. SEM observation and EDX analysis of the BCFNO and BSCFO membranes indicated that no segregation of metal ions was found for the used BCFNO membrane while the original perovskite phase of BSCFO decomposed under the experimental condition. The experimental results of oxygen permeability and stability were consistent with the analysis on the oxygen sorption property of perovskites.