Quantitative analysis on microstructure evolution of Ti-6Al-2Zr-2Sn-2Mo-1.5Cr-2Nb alloy during isothermal compression

         

摘要

Isothermal compression tests of Ti-6Al-2Zr-2Sn-2Mo-1.5Cr-2Nb alloy were conducted at a Gleeble-1500 simulator in deformation temperature range of 1103–1243K, strain rate range of 0.01–5.00 s-1and height reduction range of 50 %–70 %. The effects of processing parameters on morphology, grain size and contents of a and b phases were discussed based on the quantitative microstructure examination, and the detailed explanation was shown. The results show that b transformed matrix will obviously grow up at higher deformation temperature or lower strain rate because of low grain growth activation energies. The content of a phase will decrease at higher deformation temperature or higher strain rate due to the phase transformation. Some elongated a or b grains exist at higher strain rate, implying that the dominant softening mechanism is dynamic recovery. The effect of height reduction on b transformed matrix is negligible, but the height reduction has some effects on the morphology of primary a phase.

著录项

相似文献

  • 中文文献
  • 外文文献
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号