Microstructure and properties of joint for stirring brazing of dissimilar Al/Mg alloy during heating processes

摘要

In this paper, 2024 Al alloy and AZ31 B Mg alloy were brazed with aid of stirring without flux in air.The effects of the brazing temperature on microstructure and shear strength of the joint were investigated. The diffusion zone is found at joint interface near Al base metal,which consists of Al–Zn–Sn solid solution. At the same time, continuous intermetallic compounds(IMCs) phase and broken ones are found at joint interface near Mg base metal, which mainly consists of the Mg2 Sn phase. With the increase of the brazing temperature, the shear strength at the joint interface near Al base metal rises gradually. On the contrary, that of the joint interface near Mg base metal obviously decreases.