Effect of fabrication conditions on micros tructure and thermoelectric properties of the Bi_(1.9)Lu_(0.1)Te_3 compound was studied.Starting nanopowder with mean nanoparticle size of ~37 nm was synthesized by a microwave-solvothermal method.In order to prepare samples with various micro-grained structures,the synthesized nanopowder was compacted by two methods.The first method is cold isostatic pressing with further hightemperature annealing,while the second method is spark plasma sintering at various temperatures of process(653 and 683 K).It is found that mean grain size is equal to~290,~730 and ~1160 nm for cold isostatically pressed and spark plasma sintered at 653 and 683 K samples,respectively.The micro-grained sample with maximum mean grain size shows the best thermoelectric properties.This sample is structurally inhomogeneous and has the lowest thermal conductivity and the specific electrical resistivity.Maximum dimensionless figure of merit for this sample is equal to ~0.9 for temperature range of450-500 K.
展开▼
机译:Etude du Comportement micro-mecanique d'Une Vitroceramique a subst de siO2-al2O3-Li2O en Liaison avec la microstructure(siO2-al2O3-Li2O玻璃陶瓷的微观力学行为及其与微结构的关系研究)