在CE为4.4%~4.5%的高导热铸铁制动盘中加入不同量的铌合金,研究了Nb对其组织和力学性能的影响.结果表明,CE为4.4%、w(Nb)量为0.09%时,高导热铸铁制动盘石墨组织细化,力学性能得到一定的提高,磨损量降低,制动盘的抗热裂性提高.%Different amount of niobium alloy was added into the high thermal conductivity cast iron with CE of 4.4%~4.5% used for brake disc,and the effect of the niohium on the microstructure and mechanical properties of the casting were investigated. The result showed that,when CE was of 4.4%,Nb was of 0.09% .the graphite of the high thermal conductivity cast iron brake disc became finer,its mechanical properties were increased in some degree,its wear loss was reduced,its hot cracking resistance was improved.