防锈铝板/镀锌钢板异种金属冷金属过渡熔钎焊接头的组织与抗拉强度

摘要

The cold metal transfer (CMT) brazing-welding process was used to weld dissimilar metals of LF21 rust-proof aluminum plate and DD51D+Z zinc-coated steel plate,and the microstructure and tensile strength of the joint were studied.The results show that the compound layer of middle interface zone of the braze-weld joint was intermetallic compound FeAla with thickness of 4-6 μm.The average transverse tensile strength of the joint was up to 77 MPa and strength coefficient was 0.6.%采用冷金属过渡(CMT)熔钎焊接工艺,对LF21防锈铝板和DD51D+Z镀锌钢板进行了异种金属的连接,对接头的显微组织和抗拉强度进行了研究.结果表明:防锈铝板和镀锌钢板的熔钎焊接头的中间界面区化合物为4～6 μm厚的FeAl3金属间化合物,接头的平均横向抗拉强度为77MPa,接头的强度系数为0.6.