A new composition of Portland cement clinker was studied, in which KH, SM and IM was 0.98,2.4 and 2.4 respectively as well as its meal added 1%CuO (in mass). Fired at 1 200 ℃,1 350 ℃,1 400 ℃ and 1 450 ℃ for 30 min, the resultant mineral phases component and mineral morphology were analyzed. The performances of the cement which was made of clinker burned at 1 450 ℃ and fly ash were determined. By means of QXRD, XRD and optical microscopy, it is shown that the clinker burnt at 1 450 ℃ has the larger size crystals and distinct crystal interface, in which the C3S content is 73.37% and the mineral phases is dominantly C 3S, following by minor C2S, C3A and tetracalcium aluminoferrite. The results reveal that a new type of high C 3S content clinker can completely be made by traditional temperature-time schedule. The performances of the cement produced from this clinker with addtion of 50% fly ash and 5% gupsum were in agreement with the 32.5 strength grade of Portland fly-ash cement . The results also show that the clinker has a significant effect of saving energy and utilizing waste slag.
展开▼