Fabrication and Significant Photoelectrochemical Activity of Titania Nanotubes Modified with Thin Indium Tin Oxide Film

摘要

Ordered titanium dioxide nanotubes(Ti O_2NTs)modified with indium tin oxide(ITO)films were obtained via magnetron sputtering,in which ITO plate was used as a target,onto the as-anodized titania support followed by the calcination process.The morphology of fabricated material with deposited oxide was investigated using scanning electron microscopy.Raman and UV–Vis spectroscopies were utilized to characterize crystalline phase and optical properties of prepared samples,whereas X-ray photoelectron spectroscopy allowed determining the binding energy of present elements.In the case of titanium,three various oxidation states were identified and also the presence of indium and tin was confirmed.The electrochemical test carried out when the sample was exposed to light allows for selection of the most photoactive material.The highest photocurrent was registered when only 5-nm ITO layer was sputtered,and it equals 256and 133 l A cm^(-2)for the electrode material immersed in 0.5 M KOH and K_2SO_4electrolytes,respectively,that is accordingly 3.5 and 4.4 times higher than the one observed for pristine titania.Furthermore,ITO-modified titania exhibits excellent photostability upon prolonged illumination that is of key importance for possible application in light-driven processes.