The weldability of 12MnNiVR was examined in terms of the simulated HAZ continuous cooling transformation (SH-CCT) diagram,microstructure and mechanical properties of the simulated coarse grain heat-affected zone (CGHAZ).When t 8/5 is shorter,the microstructure mainly consists of lath bainite.When t 8/5 is 60 s,the microstructure becomes coarser bainite.Some acicular ferrite appears beside lath bainite when t 8/5 =100s.Finally,a microstructure composed of polygonal ferrite,acicular ferrite,and small amount pearlite is obtained with a small amount of bainite at t 8/5 >100s.With the increase of t 8/5,the hardness of CGHAZ decreases considerably.The minimum impact toughness of CGHAZ appears at t 8/5 =100s.The hardness and the toughness of CGHAZ remain above the specified values for steel 12MnNiVR.