Effect of Ti content on microstructure and properties of TixZrVNb refractory high-entropy alloys

摘要

This study aimed to investigate the microstructure and mechanical properties of TixZrVNb(x=1,1.5,2)refractory high-entropy alloys at room and elevated temperatures.The TiZrVNb alloy consisted of the body-centered cubic(bcc)matrix with a small amount of V2Zr phase.The Ti1.5ZrVNb and Ti2ZrVNb alloys exhibited a single-phase bcc structure.At room temperature,the tensile ductility of the as-cast alloys increased from 3.5%to 12.3%with the increase in the Ti content.The TixZrVNb alloys exhibited high yield strength at 600°C,and the ultimate yield strength was more than 900 MPa.Softening occurred at 800°C,but the ultimate yield strength could still exceed 200 MPa.Moreover,the TixZrVNb alloys displayed low densities but high specific yield strengths(SYSs).The lowest density of TixZrVNb alloys was only 6.12 g/cm^3,but the SYS could reach about 180 MPa·cm^3·g^−1,which is better than those of most reported high-entropy alloys(HEAs).