The acoustic emission(AE)characteristicsfrom the fatigue crack propagation in SM50B-Zcsteel were strongly affected by the environment me-dium.The AE feature from the fatigue process bothin air and in 3.5% NaCl aqueous solution mani-fested a periodicity which indicated the fatigue ex-tension was discontinuous.The fatigue striationand secondary cracking were the main AE sourcesduring the fatigue crack growth in air.In contrast,AE during the fatigue crack propagation in 3.5%NaCl solution was released from the intergranularfracture and quasicleavage cracking.