A synthesis method for the production of porous bulk metallic glass (BMG) was introduced. This method utilizes the su- perplastic forming ability of amorphous powder in the supercooled liquid (SCL) state and intenerating salt mixture as a placeholder to produce BMG foam by using a hot die pressing method. Scanning electron microscope (SEM), X-ray diffraction (XRD) and dif- ferential scanning calorimetry (DSC) were employed to characterize the morphologies of foaming structure, the crystallization and the percentage of crystallization of the as-produced porous BMG. The results suggested that the formation of porous structure by su- perplastic forming process is feasible. Good bonding effect was observed between amorphous powder particles. Less than 6.5% of crystalline phases were formed during hot pressing, and less than 5.5% of residual salt was enclosed in the foam. To remove any re- sidual salt particles, salt preforms with three-dimensional network and good connectivity is necessary.