Tempering mechanism of lath martensite induced in IF steel under high pressure

摘要

In this paper,low-and high-strength lath martensite(350 and 640 HV)was fabricated in an IF steel via high pressure martensitic transformation.The microstructure and the softening during their tempering from 200°C to 800°C for 1 h were systematically investigated.A carbon-irrelevant tempering process was proposed,exhibiting a three-stage structural evolution pattern depending upon the tempering de-gree(1-(HV-HV FP)/(HV NP-HV FP),where the HV is the instant hardness,HV NP is the non-tempered hard-ness and HV FP is the fully tempered hardness):(1)low tempered(50%),clearing up the remained variant laths via the migration of the triple junctions.Martensite-type microstructure is tailored by low-index lamellar variant boundaries and is thus intrinsically thermally stable,whereas the mobile terminal tips decrease the tempering resistance.The underlying mechanism for such carbon-irrelevant process was discussed and the potential effect on the tempering behavior of carbon-contained martensite was highlighted.