Mechanical,corrosion and magnetic behavior of a CoFeMn_(1.2)NiGa_(0.8) high entropy alloy

摘要

In this study,a magnetic high entropy alloy(HEA)of CoFeMn_(1.2)NiGa_(0.8)was designed and prepared by arc melting in order to investigate its mechanical,corrosion and magnetic behavior.The results show that the alloy mainly possesses body-centered cubic(BCC)phase and face-centered cubic(FCC)phase.A high compressive strength of 1450 MPa,a strain of 18.5%and a relatively low yield strength of 303MPa in as-cast condition at room temperature can be achieved in the present alloy.In-situ high-energy X-ray diffraction technique was employed to reveal the deformation mechanism of Co Fe Mn_(1.2)Ni Ga_(0.8)under uniaxial compression and the results show that the competition between BCC phase and FCC phase plays a significant role during the compressive process.The corrosion behavior of Co Fe Mn_(1.2)Ni Ga_(0.8)was investigated in 3.5 wt%Na Cl solution and it turned out that the alloy possessed good corrosion resistance.At last,the magnetic behavior of the Co Fe Mn_(1.2)Ni Ga_(0.8)alloy was studied and it can present a high saturation magnetization of 94.5 emu/g and a coercivity of 26.4 Oe at 4 K.This work indicates that the present Co Fe Mn_(1.2)Ni Ga_(0.8)HEA has promising applications as future magnetic functional materials.