In-situ synthesis of TiC/Fe alloy composites with high strength and hardness by reactive sintering

摘要

Fe alloy composites reinforced with in-situ titanium carbide(Ti C) particles were fabricated by reactive sintering using different reactant C/Ti ratios of 0.8,0.9,1 and 1.1 to investigate the microstructure and mechanical properties of in-situ Ti C/Fe alloy composites.The microstructure showed that the in-situ synthesized Ti C particles were spherical with a size of 1–3 μm,irrespective of C/Ti ratio.The stoichiometry of in-situ Ti C increased from 0.85 to 0.88 with increasing C/Ti ratio from 0.8 to 0.9,but remained almost unchanged for C/Ti ratios between 0.9 and 1.1 due to the same driving force for carbon diffusion in Ti Cxat the common sintering temperature.The in-situ Ti C/Fe alloy composite with C/Ti = 0.9 showed improved mechanical properties compared with other C/Ti ratios because the presence of excess carbon(C/Ti = 1 and 1.1) resulted in unreacted carbon within the Fe alloy matrix,while insufficient carbon(C/Ti = 0.8)caused the depletion of carbon from the Fe alloy matrix,leading to a significant decrease in hardness.This study presents that the maximized hardness and superior strength of in-situ Ti C/Fe alloy composites can be achieved by microstructure control and stoichiometric analysis of the in-situ synthesized Ti C particles,while maintaining the ductility of the composites,compared to those of the unreinforced Fe alloy.Therefore,we anticipate that the in-situ synthesized Ti C/Fe alloy composites with enhanced mechanical properties have great potential in cutting tool,mold and roller material applications.