Improving the strength and SCC resistance of an Al-5Mg-3Zn alloy with low-angle grain boundary structure

摘要

The strength of traditional Al-Mg alloys is relatively low because it mainly relies on solid solution strengthening.Adding a third component to form precipitation can improve their strength,but it usually leads to high-stress corrosion cracking(SCC)sensitivity due to the formation of high-density precipitates at grain boundaries(GBs).So far,it is still challenging to improve the strength of Al-Mg alloys without re-ducing SCC resistance.Herein,a nanostructured Al-5Mg-3 Zn alloy with a good yield strength of 336 MPa and good elongation was successfully produced.By dynamic plastic deformation and appropriate anneal-ing treatment,near-equiaxed nanograins were introduced in the nanostructured Al-5Mg-3 Zn alloy with a high proportion(71%)of the low-angle grain boundary.TEM statistical investigations show that the pre-cipitation of active T’phase at GBs has been greatly suppressed in the nanostructured Al-5Mg-3 Zn alloy at sensitized conditions,and the area fraction of GB precipitates is reduced from 72%to 21%,which sig-nificantly decreases the SCC susceptibility.This study provides guidance for developing advanced Al-Mg alloy with high SCC resistance.