Seeded growth of Ti-46Al-8Nb polysynthetically twinned crystals with an ultra-high elongation

摘要

Large size polysynthetically twinned crystals of Ti-46 Al-8 Nb alloy with a parallel lamellar microstructure were successfully prepared using a Ti-43 Al-3 Si seed by our new operation.A large amount of columnar B2 phase paralleling to the growth direction was found in the final lamellar microstructure.Higher growth rate(>30 mm/h)led to the failure of seeding process.Based on these results,a new mechanism is proposed to describe the seeding process of the hypo-peritectic Ti Al alloys.The peritecticαphase is suggested to directly nucleate from the melt,and then act as nucleus for transformedαphase in the subsequentβtoαtransformation.At the higher growth rate,the appearance ofβphase secondary dendrites and homogeneous nucleation lead to the failure of seeding process.High Nb addition leads to a large amount of residualβphase,and theseβdendrites finally evolve into B2 phase.The room temperature tensile elongation was measured to be 11.9-18.5%for Ti-46 Al-8 Nb PST crystals,which is the highest ever reported value for Ti Al based alloys.