Regulating the recrystallized grain to induce strong cube texture in oriented silicon steel

摘要

Cube texture contains two easy magnetization directionsparallel to rolling and transverse direction,respectively,which is the most ideal magnetic texture suitable not only for transformers but also for rotating machines.In this study,a strong cube texture with ODF density of 50.73 mrd was successfully obtained by regulating the recrystallized grain orientation using cross-rolling and pulsed electric current,compared to conventional thermal annealing(the average cube texture intensity is~10 mrd in lots of latest studies).Cross cold rolling process intentionally"created"metastable deformed cube orientation in oriented silicon steel and the specific recrystallization texture rotation path was identified under pulsed electric current in 5 min:{114}→{114}→{114}→{001}→{001}.The cube-oriented grains were induced by pulsed electric current(800℃)and rapid heating(51.9℃/s,750℃),while the cube grains were observed in the annealed samples at the high temperature(1060℃).Recrystallized grain size of pulsed samples is about twice that of the annealed sample.This phenomenon is considered that the concurrent effects of electron wind force and Joule heating affected the nucleation,growth and rotation of cube grains by reducing the nuclear barrier,producing higher grain boundary mobility and structural evolution towards a state with lower electrical resistance.This idea of current-controlled texture is worthy of popularization in more materials and the realization of an electromagnetic field to crystal orientation selection is an interesting topic.